Excellent Adhesiveness RTV-1 silicone sealant for solar glass
Product Quick Detail
- FOB Price
- USD $9.00 / Piece
- Place Of Origin
- China (Mainland)
- Minimum Order
- 1
- Packaging
- N/A
- Delivery
- 15 Days
Specifications
Before The Curing
| Appearance | White Paste |
| Tack Free Time | ≤10 (min) |
| Extrudability | 5~11 (g/s,25℃) |
| Cure Time | 3~7(d) |
After the curing
| Relative Density | 1.40~1.45 (g/cm3) |
| Tensile Strength | ≥2.5 (MPa) |
| Break Elongation | ≥500 (%) |
| Shear Strength | ≥2.0 (MPa) |
| Hardness | 45~55 (Shore A) |
| The Temperature Range | -60~200 (℃) |
| Volume Resistivity | 2.6×1015 (Ω·CM) |
| Dielectric Strength | 20 (kV/·mm) |
| Dielectric Constant | 3.12 |
| Flame Retardant Grade | UL94 HB |
Sample: 300mL / tube, 25tubes / box.
NOTE
After operating, the rest of glue must be sealed to store , and tightened the cap immediately. when using it in the next time, if there is a little crust in sealed place, to remove it and it will not affect the normal application. the process of storage , the canal orifices may appear the phenomenon of the curing, to clean it then it can be used again, and the performance of product is not affected.
SPECIFICATION TRANSPORT
STORAGE
1. 6 months shelf life if stored below 25 ℃ in cool, dry place, when the product passed its expiration date, it should be confirmed without abnormal phenomenon, then that can be used.
2. These products don't belong to dangerous goods, so they can be transported as normal chemicals. But be careful of leakage.
3. Ensure that it is without abnormal before being used if the products exceeding retention period.
- Country: China (Mainland)
- Business Type: 生产厂家
- Market:美洲,欧洲,欧洲联盟
- Founded Year:2001
- Address:
- Contact:Joe Lu
Other products from Guangzhou Usilicone chemical material Co.,Ltd
Relate products of Excellent Adhesiveness RTV-1 silicone sealant for solar glass
PRODUCTION CHARACTERISTICS Can be used in harsh environments for a long time The silicone sealant has the performance of superior high and low resistance, excellent insulation, high stability with thermal oxidation and ozone. It can be widely usesd in aerospace, ...
Appearance Translucent And Half Flow Relative Density 0.95~1.05 (g/cm3) Tack Free Time ≤90 (min) Completely Cure Time 3~7(d) After the curing Hardness 35~45 (Shore A) Tensile Strength ≥1.0 (MPa) Break Elongation ≥50(%) The Temperature Range -60~200 (℃) ...
Before The Curing Appearance White Paste Tack Free Time ≤10 (min) Extrudability 5~11 (g/s,25℃) Cure Time 3~7(d) After the curing Relative Density 1.40~1.45 (g/cm3) Tensile Strength ≥2.5 (MPa) Break Elongation ≥500 (%) Shear Strength ≥2.0 (MPa) Hardness ...
Before the curing Appearance White paste Relative density 1.60~1.70(g/cm3) Surface drying time â¤15(min) After the curing Tensile strength â¥1.5(MPa) Elongation At Break â¥150(%) Shear strength â¥2.0(MPa) Hardness 35~45(Shore A) Temperature Range ...