Appearance | Translucent And Half Flow |
Relative Density | 0.95~1.05 (g/cm3) |
Tack Free Time | ≤90 (min) |
Completely Cure Time | 3~7(d) |
After the curing
Hardness | 35~45 (Shore A) |
Tensile Strength | ≥1.0 (MPa) |
Break Elongation | ≥50(%) |
The Temperature Range | -60~200 (℃) |
Volume Resistivity | ≥1.0×1014 (Ω·CM) |
Dielectric Strength | ≥18 (kV/·mm) |
Sample: 1kg/tin (which may be decided according to user's need)
Effectively prolong the service life of electronic components
Before The Curing Appearance White Paste Tack Free Time ≤10 (min) Extrudability 5~11 (g/s,25℃) Cure Time 3~7(d) After the curing Relative Density 1.40~1.45 (g/cm3) Tensile Strength ≥2.5 (MPa) Break Elongation ≥500 (%) Shear Strength ≥2.0 (MPa) Hardness ...