During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all defects.

The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ferrules, if the process is not proper, the cracks may be directly caused or the hidden cracks may be buried for the occurrence of the lap ring grinding cracks.

There are many ways to form cracks in bearing rings: Raw material defects include: cracks in raw materials and the effects of raw material defects on the grinding process.

Forging defects include forging cracks, effects of forged microstructure defects on the grinding process, and cutter cracks. There are also various heat treatment defects and the like. Therefore, crack detection and hardness testing are essential. As one of the experienced non destructive testing equipment manufacturers, BKN offers the perfect combination of Bearing Ring Crack and Hardness Combination testing equipment. Our advanced crack testing equipment enable accurate and efficient crack detection, ensuring the quality and integrity of forged components.

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 Brief Introduction

Detection process

Vibrating plate and string charging →hardness test→crack detection→automatic blanking


Bad product sorting

Automatic charging —automatic detection—automatic sorting —automatic blanking

Crack sensitivity: a crack with a depth of ≥0.05 mm and a length of ≥1 mm extending inward from the surface of the ferrule; for a crack that has not extended to the surface inside the ferrule, when the thickness between the subcutaneous surface and the surface of the workpiece is ≤0.2 mm, the depth is ≥0.20 mm Cracks of length ≥ 1 mm can be detected.

Hardness sensitivity: Rockwell 1HRC ~ 2HRC (other parameters remain stable and consistent).

  • Country: China (Mainland)
  • Business Type: Manufacturer
  • Market:Americas
  • Founded Year:
  • Address:
  • Contact:bkneddy .com
more images of Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
*Your name:
*Your Email:
*To:Nanjing BKN Automation System Co.,LTD
*Subject:
*Message:
Enter between 20 to 3,000 characters. English only.     Characters : 0 / 3000
*Enter the secure code shown below Mfrbee security Image      Reload Image

submiting now We do inquire for you , please wait ...

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02

During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all defects. The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ...

Nanjing BKN Automation System Co.,LTD

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02

During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all defects. The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ...

Nanjing BKN Automation System Co.,LTD