Product Description

High Quality Aluminum Sheet and Coil 5005 From China

5005 aluminum sheet/coil of Mingtai Al. is certificated to ASTM, EN as well as JIS, etc. and it can be cut to sizeat customers’ need. Mg is the principal element in the 5005 aluminum sheet/coil and when it used as main alloying element or combined with Mn, high strength and no-heat treatable properties can be realized. 5005 aluminum sheet/coil of Mingtai Al. has many tempers available, such as 5005-H12, 5005-H14, 5005-H16, 5005-H18,5005-H22, 5005-H24, 5005-H32, 5005-H34, 5005-H36, 5005-H38, etc.

http://www.aluminium-sheet-price.com/aluminium_sheet/

Elements	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Others	Al
Content	0.3	0.7	0.2	0.2	0.5-1.1	0.1	0.25	-	0.15	Remain
Alloy Temper	Specified thickness	Tensile strength	Yield strength	Elongation
(MPa)	(MPa)	(%)
5005-H34 or 5005-H24	0.2~0.63mm	138.179	Min104	min 3
0.63~1.2mm	min 4
1.2~6.3mm	min 5
6.3~50mm	min 8
5005-H32 or 5005-H22	0.2~600mm	118-158	Min83	min 3

5005-H14	145-186	min118	min1

Features&Application

The main content of 5005 aluminum sheet/coil is Fe, Mg and Si, thus, it has good weld-ability and resistance to correction (especially when anodized), which resulting in suitable for marine applications. 5005 aluminum sheet/coil is also a non-heat treatable alloy and it can be strengthened (hardened) by cold working. However, hot working should not normally be necessary. Besides, it scores well in formability, especially in softer tempers. The machinability of 5005 aluminum sheet/coil is generally fairly poor. 5005-H34 and 5003-H38 can be machined, but with much more difficult than many other aluminum alloys.